Gradient Material Fabricated via Accumulative Skin Pass Rolling and Related Microstructure and Mechanical Characterization

Download (9.93 MB)
thesis
posted on 2024-11-12, 13:56 authored by Dongzhi Luo
Significant efforts have been made in recent years to improve the ductility of ultra-fine grained/nanograined (UFG/NG) materials while preserving their high strength. Fabricating materials with gradient structures has been regarded as an effective approach to improving both ductility and strength. The sizes of the gradient material samples fabricated by the existing methods are limited. To date, a large-scale industrial application has not been reported due to a lack of reliable technologies capable of producing such materials at large volumes. In this thesis, a process using the Accumulative Skin-Pass Rolling (ASPR) technique was developed to fabricate the large-volume metallic strips with gradient structure. The mechanical properties and microstructure in the ASPR processed aluminium (AA6061) and copper were systematically investigated. The effects of three ASPR process, namely, the friction at the roll/sample interface, roll speed ratio and thickness reduction par pass parameters, on the mechanical properties and microstructure were investigated.

History

Year

2018

Thesis type

  • Doctoral thesis

Faculty/School

School of Mechanical, Materials, Mechatronic and Biomedical Engineering

Language

English

Disclaimer

Unless otherwise indicated, the views expressed in this thesis are those of the author and do not necessarily represent the views of the University of Wollongong.

Usage metrics

    Categories

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC