Formation of austenite grain structure accompanying hot rolling of Nb-V and Nb-V-Ti microalloyed steels

Download (20.19 MB)
thesis
posted on 2024-11-11, 10:52 authored by Muhammad Irfan
An investigation of the grain coarsening characteristics has been carried out on samples of commercial C-Mn, Nb-V and Nb-V-Ti steels produced at PT. Krakatau Steel, Indonesia. The results have shown that the grain coarsening occurs at a low temperature in the cast C-Mn steel, which seems to be due to the low temperature of solution of the AIN grain boundary pinning particles. It was found that the grain coarsening temperature (GCT) can be raised by microalloy additions of Nb- V and Nb-V-Ti. Austenite structural evolution after single-pass rolling has also been investigated in the above steels, in the range of reductions from 20% to 60% and at temperatures of 950°C - 1150°C. The experimental procedure involved first heating the samples to 1200°C for 15 minutes, cooled to various temperatures (950°C - 1150°C), rolled and then subsequently quenching after the samples were held at the selected temperature for different times (3 -1800 sec.).

History

Year

1995

Thesis type

  • Masters thesis

Faculty/School

Department of Materials Engineering

Language

English

Disclaimer

Unless otherwise indicated, the views expressed in this thesis are those of the author and do not necessarily represent the views of the University of Wollongong.

Usage metrics

    Categories

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC