Performance evaluation of CNT/polypyrrole/Mn02 composite electrodes for electrochemical capacitors
journal contribution
posted on 2024-11-16, 06:24authored byGordon WallaceGordon Wallace, Byung Kim, S R Sivakkumar, Dong Young Kim, Jang Myoun Ko
A ternary composite of CNT/polypyrrole/hydrous MnO2 is prepared by in situ chemical method and its electrochemical performance is evaluated by using cyclic voltammetry (CV), impedance measurement and constant-current charge/discharge cycling techniques. For comparative purpose, binary composites such as CNT/hydrous MnO2 and polypyrrole/hydrous MnO2 are prepared and also investigated for their physical and electrochemical performances. The specific capacitance (SC) values of the ternary composite, CNT/hydrous MnO2 and polypyrrole/hydrous MnO2 binary composites estimated by CV technique in 1.0 M Na2SO4 electrolyte are 281, 150 and 35 F g−1 at 20 mV s−1 and 209, 75 and 7 F g−1 at 200 mV s−1, respectively. The electrochemical stability of ternary composite electrode is investigated by switching the electrode back and forth for 10,000 times between 0.1 and 0.9 V versus Ag/AgCl at 100 mV s−1. The electrode exhibits good cycling stability, retaining up to 88% of its initial charge at 10,000th cycle. A full cell assembled with the ternary composite electrodes shows a SC value of 149 F g−1 at a current loading of 1.0 mA cm−2 during initial cycling, which decreased drastically to a value of 35 F g−1 at 2000th cycle. Analytical techniques such as scanning electron microscopy (SEM), X-ray diffraction spectroscopy (XRD), Brunauer–Emmet–Teller (BET) surface area measurement and inductively coupled plasma-atomic emission spectrometry (ICP-AES) are also used to characterize the composite materials.
Sivakkumar, S. R., Ko, J., Kim, D., Kim, B. C. & Wallace, G. G. (2007). Performance evaluation of CNT/polypyrrole/Mn02 composite electrodes for electrochemical capacitors. Electrochimica Acta, 52 (25), 7377-7385.