Correlations between the structure and superconducting properties of MT-YBaCuO

Download (1.37 MB)
journal contribution
posted on 2024-11-15, 21:45 authored by Tetiana Prikhna, V Moshchill, J Rabier, X Chaud, A Joulain, Oleksiy PanOleksiy Pan, D Litskendorf, T Habisreuther
© Published under licence by IOP Publishing Ltd. Comprehensive experimental results of fully oxidized (up to YBa2Cu3O6,9-7) melt-Textured YBaCuO materials with different microstructures are presented. These microstructures are built respectively: (1) with a high dislocations density but almost without twins (after high temperature treatment at 2 GPa) and (2) with a high twin density, but practically free from dislocations and stacking faults (after high temperature oxygenation at 10-16 MPa). It is shown that for attaining high critical current densities and fields of irreversibility (jc(H-c, 0 T)=9•104 A/cm2, H irr=9.7 T at 77 K), a high twin density in YBa2Cu3O6.9-7 matrix of MT-YBCO is required. The density of twins in fully oxidized materials depends on the distances between Y2BaCuO5 inclusions, larger twin densities are related to shorter distances between inclusions. The influence of phase composition of the initial powder mixtures on the distances between Y2BaCuO5 inclusions have been characterized and discussed.

History

Citation

Prikhna, T., Moshchill, V., Rabier, J., Chaud, X., Joulain, A., Pan, A., Litskendorf, D. & Habisreuther, T. (2020). Correlations between the structure and superconducting properties of MT-YBaCuO. Journal of Physics: Conference Series, 1559 (1),

Language

English

RIS ID

144517

Usage metrics

    Categories

    Keywords

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC