Carbothermal reduction of titania in different gas atmospheres

Download (506.73 kB)
journal contribution
posted on 2024-11-15, 05:03 authored by Mohammad Dewan, Guangqing ZhangGuangqing Zhang, Oleg Ostrovski
The synthesis of titanium oxycarbide by carbothermal reduction of titania was studied in hydrogen, argon, and helium in isothermal and temperature programmed reduction experiments in a tube reactor with continuously flowing gas. In the temperature range of 1000 C to 1500 C, the reduction rate increased with increasing temperature. Formation of titaniumoxycarbide started at 1200 C in all three gases. The reduction was the fastest in hydrogen. Formation of titanium oxycarbide in hydrogen was close to completion in 120 minutes at 1300 C, 60 minutes at 1400 C, and less than 30 minutes at 1500 C. The reduction in argon and helium had similar rates and reached 90 to 95 pct after a 300-minute reduction at 1400 C to 1500 C. Faster carbothermal reduction of titania in hydrogen than in argon and helium was attributed to involvement of hydrogen in the reaction. Hydrogen reduced titania to titanium suboxides and reacted with carbon, forming methane, which reduced titaniumsuboxides to titaniumoxycarbide. Titanium oxycarbide synthesized in hydrogen for 180 minutes at 1300 C contained 13 mol pct TiO. At 1500 C, oxygen concentration decreased to a degree corresponding to 1.4 mol pct TiO. In the titanium oxycarbide produced by a 300-minute reduction at 1600 C, the TiO content was 0.6 mol pct.

History

Citation

Dewan, M. A. R., Zhang, G. & Ostrovski, O. (2009). Carbothermal reduction of titania in different gas atmospheres. Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science, 40 (1), 62-69.

Journal title

Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science

Volume

40

Issue

1

Pagination

62-69

Language

English

RIS ID

62894

Usage metrics

    Categories

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC