An EBSD Study on the Stability of Retained Austenite in Low-Si TRIP Steels During Uniaxial Tension

journal contribution
posted on 2024-11-17, 13:24 authored by Fayez Al-Harbi, Azdiar A Gazder, Elena Pereloma
Two transformation-induced plasticity steels, with and without Nb–Ti additions, were subjected to uniaxial tension after simulated thermo-mechanical processing. Electron back-scattering diffraction, with phase segmentation implemented during post-processing, was used to investigate the stability of retained austenite (RA) by analyzing its size, morphology, and neighboring phases. The rate of RA transformation to martensite was higher in the Nb–Ti-containing steel than in the base steel as most RA was co-located between bainitic ferrite with parallel arrangement of laths in the former steel. Depending on the location of RA and the developed stress state, its stability in tension declines in the following order: RA in bainite > RA at polygonal ferrite/bainite interfaces > RA embedded in polygonal ferrite grains and at polygonal ferrite triple junctions or grain boundaries. Fine grains of RA may be less stable than their coarser counterparts if they are located in unfavorable stress regions of the microstructure.

History

Journal title

JOM

Volume

73

Issue

11

Pagination

3169-3180

Language

English

Usage metrics

    Categories

    No categories selected

    Keywords

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC