Title

Sensing capabilities of graphite based MR elastomers

RIS ID

35733

Publication Details

Tian, T., Li, W. & Deng, Y. (2011). Sensing capabilities of graphite based MR elastomers. Smart Materials & Structures, 20 (25022), 1-7.

Abstract

This paper presents both experimental and theoretical investigations of the sensing capabilities of graphite based magnetorheological elastomers (MREs). In this study, eight MRE samples with varying graphite weight fractions were fabricated and their resistance under different magnetic fields and external loadings were measured with a multi-meter. With an increment of graphite weight fraction, the resistance of MRE sample decreases steadily. Higher magnetic fields result in a resistance increase. Based on an ideal assumption of a perfect chain structure, a mathematical model was developed to investigate the relationship between the MRE resistance with external loading. In this model, the current flowing through the chain structure consists of both a tunnel current and a conductivity current, both of which depend on external loadings. The modelling parameters have been identified and reconstructed from comparison with experimental results. The comparison indicates that both experimental results and modelling predictions agree favourably well.

Please refer to publisher version or contact your library.

Share

COinS
 

Link to publisher version (DOI)

http://dx.doi.org/10.1088/0964-1726/20/2/025022