Analysis of {411} <148> recrystallisation texture in twin-roll strip casting of 4.5 wt% Si non-oriented electrical steel

Authors

Guoqing Zu, University of Wollongong (UOW)
Xiaoming Zhang, Northeastern UniversityFollow
Jingwei Zhao, University of WollongongFollow
Yuqian Wang, Northeastern University
Yi Cui, Northeastern University
Yi Yan, University of WollongongFollow
Zhengyi Jiang, University of WollongongFollow

RIS ID

108004

Publication Details

Zu, G., Zhang, X., Zhao, J., Wang, Y., Cui, Y., Yan, Y. & Jiang, Z. (2016). Analysis of {411} recrystallisation texture in twin-roll strip casting of 4.5 wt% Si non-oriented electrical steel. Materials Letters, 180 63-67.

Abstract

The evolution of {411} texture in a promising twin-roll strip casting of 4.5 wt% Si electrical steel was skillfully investigated. The results show that the selective growth mechanism, caused by orientation pinning, is responsible for the formation of the sharp {411} component which is beyond the preferred nucleus spectrum.