Chemical solution deposition and transport properties of La1-xNaxMnO3 films on YSZ substrates

RIS ID

24915

Publication Details

Zhu, X, Shi, D, Zhang, L, Sun, Y, Song, W, Wang, L, Silver, TM & Dou, SX (2008), Chemical solution deposition and transport properties of La1-xNaxMnO3 films on YSZ substrates, Journal of Alloys and Compounds, 459(1-2), pp. 83-86.

Abstract

Monovalent Na-doped LaMnO3 films (La1−xNaxMnO3) were prepared on single crystal YSZ substrates using chemical solution deposition, which is a low-cost method for large-area film preparation. It was observed that the derived La1−xNaxMnO3 films were highly (h 0 0)-oriented, which was different from the case of previously reported colossal magnetoresistance films on YSZ substrates. The transport properties clearly suggested that the La1−xNaxMnO3/YSZ films behaved like epitaxial films, and the relatively large low-field magnetoresistance at 300 K, 5% at 0.5 T, suggest that it would be interesting to further study the Na-doped LaMnO3 systems.

Please refer to publisher version or contact your library.

Share

COinS
 

Link to publisher version (DOI)

http://dx.doi.org/10.1016/j.jallcom.2007.05.053